Incoloy 825 (UNS N08825) is a molybdenum- and copper-bearing nickel-iron-chromium alloy, titanium stabilised. It combines resistance to sulphuric and phosphoric acid, seawater and stress-corrosion cracking, making it a workhorse for sour oil and gas, chemical heat exchangers and nuclear fuel reprocessing.
Shanghai Hangbo Alloy Group Co., Ltd. supplies Incoloy 825 Seamless Tube & Pipe to ASTM B163 / B423 tube — Pierced then cold-rolled / cold-drawn seamless tubing to ASTM B444, B622, B163, B165 and B861 — 100% hydrostatic or eddy-current tested for high-pressure, high-temperature and corrosive service. All material ships with EN 10204 3.1 certified mill test reports.
Sizes & Specifications
| Item | Specification |
|---|---|
| Outside diameter | φ6 – 630 mm |
| Wall thickness | 0.5 – 40 mm |
| Length | ≤ 18 m / custom lengths on request |
| NDT inspection | ET / UT / Hydrostatic 100% |
| Common standards | ASTM B444, B622, B163, B165, B861, B338 |
Incoloy 825 Chemical Composition (wt%)
| Element | Content (wt%) | Element | Content (wt%) |
|---|---|---|---|
| Ni (镍) | 38.0–46.0 | Ti (钛) | 0.60–1.20 |
| Cr (铬) | 19.5–23.5 | Al (铝) | ≤ 0.20 |
| Fe (铁) | ≥ 22.0 | C (碳) | ≤ 0.05 |
| Mo (钼) | 2.5–3.5 | Mn (锰) | ≤ 1.00 |
| Cu (铜) | 1.50–3.00 | Si (硅) | ≤ 0.50 |
Incoloy 825 Mechanical Properties
| Property | Value |
|---|---|
| Tensile strength (Rm) | ≥ 586 MPa |
| Yield strength (Rp0.2) | ≥ 241 MPa |
| Elongation (A) | ≥ 30 % |
| Hardness | ≤ 190 HB |
| Density | 8.14 g/cm³ |
| Melting range | 1370–1400 °C |
| Thermal conductivity | 11.1 W/m·K |
| Young's modulus | 196 GPa |
| Max service temperature | 1000 °C |
Typical Applications
- Sour oil and gas tubing, valves and heat exchangers
- Sulphuric acid pickling and acid recovery
- Nuclear fuel reprocessing dissolvers
- Seawater coolers and marine piping
- Chemical process piping and vessels
Why Buy from Hangbo Alloy?
- Factory-direct manufacturer — founded 2012, headquartered in Shanghai Songjiang
- Cut-to-size service — bars cut to length, plates flame/plasma/laser-cut, tubes cut and bevelled to drawing
- Certified quality — ISO 9001:2015, GB/T 19001-2016, GJB 9001C-2017, EN 10204 3.1 certificates
- Complete mill documentation — chemical analysis, mechanical test, UT, hardness and grain-size reports with every shipment
Contact Us — Shanghai Hangbo Alloy Group Co., Ltd.
Shanghai Hangbo Alloy Group Co., Ltd.
📍 4F, Building 22, No. 85 Mingnan Road, Songjiang District, Shanghai 201613, China
📞 Tel / WhatsApp: +86 15618279078
✉️ Email: demi@nickel-alloy.com
🕒 Available 24 hours a day, 7 days a week — enquiries answered around the clock.
Send your drawing or enquiry (grade, form, size, quantity, standard) for a same-day quotation.
Continue reading
- Titanium Grade 5 (Ti-6Al-4V) Round Bar: Composition, Mechanical Properties & SupplierTitanium Grade 5 (Ti-6Al-4V) round bar (R56400) supplier: composition, aged properties, sizes and tolerances.
- 316L Seamless Pipe: Standards, Sizes and Limits316L seamless pipe (UNS S31603): ASTM A312/A269/A270 coverage, common sizes, tolerances and the corrosion limi
- A286 Round Bar: UNS S66286 Properties and LimitsA286 (UNS S66286) round bar to AMS 5731 and AMS 5737: chemistry, aged strength and where the iron-base superal
- ASTM B366 Nickel Alloy Pipe Fittings Grade GuideASTM B366 nickel alloy fittings: WP grade table, WP-S and WP-W classes, wall thickness, PMI and how they diffe
- Alloys for Bellows and Expansion JointsBellows alloy selection for expansion joints: how to choose 625, C-276, 800 or 316L strip for fatigue life, co
- All 17 Product Forms & Specifications guides
Frequently asked questions
What is the MOQ and lead time?
MOQ is flexible — trial orders from a single piece or single plate are welcome. Stock sizes ship in 3–7 days; custom-cut, forged or machined items typically 15–35 days.
Can you provide third-party inspection and shipping to my port?
Yes. SGS / BV / TUV or your nominated inspector can witness all tests before shipment. Full export documentation, sea or air freight on FOB, CIF or DDP terms.
Do you supply machining to drawing?
Yes — CNC turning, milling, drilling, grinding and wire-cut from raw material to finished part in one factory, fewer hand-offs and less material waste.